Experimental Study on Production Process of High Performance Alloyed Double Zero Aluminum Foil

2017/5/8 13:43:36

Through the above tests, we can see that 8011 alloy double zero foil than the 1235 alloy double zero foil has a more ideal surface quality, but the number of pinholes is too much, the specific reason for the 8011 alloy silicon content And therefore, in the alloy composition, but also need to make some adjustments. The application of uniform annealing process has good effect on the number of pinholes of 1235 alloy and 80l1 alloy double zero foil, but the effect of double sheet aluminum foil surface quality is different. Which is not obvious on the impact of 1235 alloy double zero foil, the impact of 8011 alloy double zero foil is very large. The 8006 alloy application, can effectively speed up the rolling speed, improve production efficiency. At the same time, 8006 alloy double zero foil surface quality is very good, the dark side of the vertical stripes is not obvious, the number of pinholes can be controlled within 100 per square meter, while more than 1235 alloy and 8011 alloy double zero foil more excellent mechanical properties The

Conclusion: High performance alloying double zero aluminum foil in the current social and industrial production which have a very wide range of uses, in many different areas, have played an important role. At present, the production of alloying double-zero aluminum foil material mainly 1235 alloy, 8011 alloy, 8006 alloy. Through the design of the test can be seen, the use of 8006 alloy high-performance alloying double-zero aluminum foil production process has many advantages, and through the production process to produce aluminum foil products in all aspects of performance and quality are ideal, so should To promote the application.